E-Z WELD - PVC Cement Regular Body, Clear 202 fast set PVC/uPVC cement for use on pipe and fittings 120/240/475/473ML

•
E-Z weld 202 EZ1 PVC Cement -473ML

Clear, regular body, fast set PVC / uPVC cement for use on pipe and fittings up to 4” (110 mm) for schedule 40
To be used for plumbing, electrical conduit, non-pressure pool and spa and PVC foam core pipe
Meets ASTM D2564
For superior joint use with E-Z Weld Primer, Purple (No.212) or Clear (No. 211). Never add thinner or additive. Never use the cement if it is stringy or jelly like. Always follow instructions on the label.
Application:
Clear, Regular Body PVC / uPVC cement for use on up to 4” (110
mm) diameter for Schedule 40. Formulated for plumbing, electrical
conduit, pool & spa. For superior joint use with E-Z Weld Primer,
Purple (No.212) or Clear (No. 211). Never add thinner or additive.
Never use the cement if it is stringy or jelly like.
Always follow instructions on the label.
Application temperature: 32°F to 110°F (0°C to 43°C).
Storage temperature: 45°F to 110°F (7°C to 43°C).
ASTM has developed the following schedule and may be used as a
guide (for relative humidity 60% or less. Sch. 40 size pipe.) e.g. a 2”
pipe size joint made at 55°F, 50% Relative Humidity and a test
pressure of 100 psi would require a cure time of 4 hrs.
Certification:
This product is tested, certified and approved by NSF International
for use on drain, waste and potable water systems. It is also listed
by the International Association of Plumbing & Mechanical Ocials
(IAPMO). It carries the Uniform Plumbing Code (UPC) seal. This
cement meets ASTM Standard D2564.
Quality Assurance:
Every batch of cement is carefully checked and monitored to assure
consistently high quality standards. Records of every batch are
kept. All ingredients are purchased from approved suppliers. This
cement has passed the following test (performed in accordance
with ASTM Std. D2564):
Lap Shear:
• 250 psi (2.76 Mpa) after 2-hour cure time at 73°F (23°C)
• 500 psi (3.45 Mpa) after 16-hour cure time at 73°F (23°C)
• 900 psi (6.20 Mpa) after 72-hour cure time at 73°F (23°C)
Hydrostatic Burst:
• 400 psi (2.76 Mpa) after 2-hour cure time at 73°F (23°C)